点击图片查看原图
是否进口 ：否
厂家(产地) ：三井化学
牌号 ：C430N
加工级别 ：注塑级
特性级别 ：耐高温,增强级
用途级别 ：通用级,汽车部件,纤维
销售方式 ：*经销
* ：三井化学
类型 ：标准料
ARLEN™ C430N聚酰胺 6T30% 玻璃纤维增强材料Mitsui Chemicals, Inc.产品说明：ARLEN™ C430N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ C430N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating.Features:High dimensional stabilityHigh melting pointHigh rigidityMinimum water absorptionGood chemical and heat resistanceFlame retardant
Applications:
Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals. 附加功能
| PDF物性文档 |
| 查找替代物 |
| 加入收藏 |
基本信息
| 填料/增强材料 | 玻璃纤维增强材料, 30% 填料按重量 |
| 添加剂 | 阻燃性 |
| 特性 | Good Heat ResistanceHigh Dimensional Stability刚性，高耐化学性良好吸水低或不吸水阻燃性 |
| 用途 | 电气/电子应用领域开关连接器 |
| 加工方法 | 注射成型 |
物理性能额定值单位制测试方法
| 比重 | 1.66 | g/cm3 | ASTM D792 |
| 收缩率 | ASTM D955 | ||
| 流动 | 0.30 | % | ASTM D955 |
| 横向流动 | 0.70 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr, 65%r.h) | 2.0 | % | ASTM D570 |
硬度额定值单位制测试方法
| 洛氏硬度 (M 级) | 95 | ASTM D785 |
机械性能额定值单位制测试方法
| 抗张强度 | 170 | MPa | ASTM D638 |
| 伸长率 (断裂) | 3.0 | % | ASTM D638 |
| 弯曲模量 | 11400 | MPa | ASTM D790 |
| 弯曲强度 | 250 | MPa | ASTM D790 |
冲击性能额定值单位制测试方法
| 悬壁梁缺口冲击强度 | 85 | J/m | ASTM D256 |
热性能额定值单位制测试方法
| 载荷下热变形温度 (1.8 MPa, 未退火) | 295 | °C | ASTM D648 |
| 玻璃转化温度 | 85.0 | °C | |
| 熔融温度 | 310 | °C | |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 | 1.2E-5 | cm/cm/°C | ASTM E831 |
| 横向 | 9.2E-5 | cm/cm/°C | ASTM E831 |
电气性能额定值单位制测试方法
| 体积电阻率 | 1.0E+15 | ohms·cm | ASTM D257 |
| 介电强度 | 26 | kV/mm | ASTM D149 |
| 介电常数 (1 MHz) | 4.00 | ASTM D150 | |
| 耗散因数 (1 MHz) | 0.013 | ASTM D150 |
可燃性额定值单位制测试方法
| UL 阻燃等级 | V-0 |